DIN 1.2379 Cold Work Steel
- Shizhang Steel
- China
- 7-30days
- 500 Tons/Month
DIN 1.2379 steel is Ledeburitic 12% chrome steel, very high resistanceagainst abrasive and adhesive wear due to a highvolume of hard carbides in the steel matrix, goodtoughness,very gooddimensional stability, highcompressive strength, very good base material forPVD/CVD coating as well as nitriding due to itssecondary hardening properties.
Product Name: COLD WORK TOOL STEEL---1.2379
Similar steel grades:
U.S.A | ASTM D2 |
German | DIN 1.2379 |
Japan | JIS SKD11 |
Sweden | -- |
China | Cr12Mo1V1 |
Chemical Composition(%) :
C | Si | Mn | Cr | Mo | P | S |
1.50-1.60 | 0.10-0.40 | 0.15-0.45 | 11.0-12.0 | 0.60-0.80 | 0.03max | 0.03max |
Principal Feature:
DIN 1.2379 steel is versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure.
Typical Application:
DIN 1.2379 steel can be used to cutting, punching, stamping tools, shear blades, thread rolling dies, cold extrusion dies, drawing and bending tools, flanging and straightening rolls, fine cutting tools deep drawing tools, plastic moulds for abrasive polymers
Heat Treatment:
Forge: at 900℃-1100℃ Cool slowly and anneal immediately
Annealing: at 830℃-860℃ Cool slowly in furnace
Stress Relieving: at to 650℃-700℃ Cool in furnace or still air
Hardening: Preheat at 650℃-850℃ raise to 1000℃-1050℃ Cool in air, oil or into hot bath held at 500℃-550℃ and then air cool
Size available:
Bars | Turned | Dia 20-500mm |
Black | Dia 20-500mm | |
Flats | Milled | T: 8-300 W: 210-610mm |
Black | T: 8-300 W: 210-610mm |
We can provide professional steel as per your detail requirement!