Cr12Mo1V1 Cold Work Steel
- Shizhang Steel
- China
- 7-30days
- 500 Tons/Month
Cr12Mo1V1 is a widely used high-carbon, high-chromium cold work die steel in the world. It is a ledeburite steel with high hardenability, hardenability and high wear resistance. It has good high-temperature oxidation resistance and is resistant to corrosion after quenching and polishing. It has good corrosion resistance and small heat treatment deformation.The corresponding foreign brand of H13 is ASTM D2、DIN 1.2379、JIS SKD11
Product Name: COLD WORK TOOL STEEL---Cr12Mo1V1
Similar steel grades:
U.S.A | D2 |
German | DIN 1.2379 |
Japan | JIS SKD11 |
Sweden | -- |
China | Cr12Mo1V1 |
Chemical Composition(%) :
C | Si | Mn | Cr | Mo | P | S |
1.50-1.60 | 0.10-0.40 | 0.15-0.45 | 11.0-12.0 | 0.60-0.80 | ≤0.03 | ≤0.03 |
Principal Feature:
Cr12Mo1V1 Cold Work Tool Steel is versatile high-carbon, high-chromium, air-hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium-rich alloy carbides in the microstructure.
Typical Application:
Cutting, punching, stamping tools, shear blades, thread rolling dies, cold extrusion dies, drawing and bending tools, flanging and straightening rolls, fine cutting tools deep drawing tools, plastic moulds for abrasive polymers
Heat Treatment:
Forge: at 900℃-1100℃ Cool slowly and anneal immediately
Annealing: at 830℃-860℃ Cool slowly in furnace
Stress Relieving: at to 650℃-700℃ Cool in furnace or still air
Hardening: Preheat at 650℃-850℃ raise to 1000℃-1050℃ Cool in air, oil or into hot bath held at 500℃-550℃ and then air cool
Size available:
Bars | Turned | Dia 20-500mm |
Black | Dia 20-500mm | |
Flats | Milled | T: 8-300 W: 210-610mm |
Black | T: 8-300 W: 210-610mm |
We can provide professional steel as per your detail requirement!