4Cr3Mo3SiV Hot Work Mold Steel
- Shizhang Steel
- China
- 15-45days
- 500 Tons/Month
4Cr3Mo3SiV Hot Work Mold Steel is H10 steel imported from the United States. It has good hardenability, toughness and high temperature hardness. 4Cr3Mo3SiV alloy tool steel can replace 3Cr2W8V and other steels to make hot stamping dies, hot forging dies, hot rolling dies and plastic pressing dies, etc. Its performance and service life are higher than 3Cr2W8V steel.Our company provides 4Cr3Mo3SiV round rods and 4Cr3Mo3SiV steel plates
Product Name: STAINLESS STEEL---4Cr3Mo3SiV
Similar steel grades:
U.S.A | H10 |
German | - |
Japan | - |
Austria | - |
Sweden | - |
China | 4Cr3Mo3SiV |
Chemical composition:
Standard | C | Si | Mn | S | P | Cr | Mo | V |
GB/T 1299-1985 | 0.35～0.45 | 0.80～1.20 | 0.25～0.70 | ≤0.03 | ≤0.03 | 3.00～3.75 | 2.00～3.00 | 0.25～0.75 |
Principal Feature:
4Cr3Mo3SiV Hot Work Mold Steel is H10 steel imported from the United States. It has good hardenability, toughness and high temperature hardness. 4Cr3Mo3SiV alloy tool steel can replace 3Cr2W8V and other steels to make hot stamping dies, hot forging dies, hot rolling dies and plastic pressing dies, etc. Its performance and service life are higher than 3Cr2W8V steel.
Typical Application:
4Cr3Mo3SiV is used to make hot roller forging dies, plastic pressing dies, hot forging dies, hot stamping dies, etc.It is also used as structural parts for aircraft, rockets and other heat-resistant operating temperatures of 400 to 500°C.
Heat Treatment:
Quenching, preheating at 790±15℃, heating at 1010±6℃ (salt bath) or 1020±6℃ (furnace controlled atmosphere), holding for 5~15min, air cooling, and tempering at 550℃.
Size available:
Bars | Turned | Dia 90-505mm |
Black | Dia 60-550mm | |
Flats | Milled | T: 70-320 W: 90-1000mm |
Black | T: 50-320 W: 90-1000mm |
We can provide professional steel as per your detail requirement!